SEALINE

Thinner for Polyurethan 2K provide appropriate application parameters such as flow, pot life and drying time. Adequate thinning level enables for different application methods.

Thinner for Polyurethan 2K provide appropriate application parameters such as flow, pot life and drying time. Adequate thinning level enables for different application methods.

Thinner for 2K epoxy primer ensure adequate application parameters such as flow, pot life and drying time. An appropriate thinning level allows for different application methods: brush, roll, spray gun.

Thinner for 2K epoxy primer ensure adequate application parameters such as flow, pot life and drying time. An appropriate thinning level allows for different application methods: brush, roll, spray gun.

SELF POLISHING ALUPLUS ANTIFOULING new generation biocide based paint, designated for sailing and motor boats, moving at a maximum speed of 40 knots. The paint’s efficiency and effectiveness is 30% higher than for traditional products.

• Category: production, care and maintenance
• Surface: laminate, wood, steel, aluminum
• Area: below waterline
• Color: white, navy blue, black
• Theoretical coverage: 11-12 m²/l for 50µm DTF
• Application: brush, roll
• Touch dry: 1 hour
• Launching time: minimum 12 hours after painting
• Advantages: can be used on vessels or elements made of aluminum, high efficiency

SELF POLISHING ALUPLUS ANTIFOULING new generation biocide based paint, designated for sailing and motor boats, moving at a maximum speed of 40 knots. The paint’s efficiency and effectiveness is 30% higher than for traditional products.

• Category: production, care and maintenance
• Surface: laminate, wood, steel, aluminum
• Area: below waterline
• Color: white, navy blue, black
• Theoretical coverage: 11-12 m²/l for 50µm DTF
• Application: brush, roll
• Touch dry: 1 hour
• Launching time: minimum 12 hours after painting
• Advantages: can be used on vessels or elements made of aluminum, high efficiency

Transparent 1K (1-component) varnish dedicated for wooden boats and yachts. Yacht Varnish is characterized by great flow, UV rays resistance and high gloss.

• Category: production, repair
• Surface: wood, paints and varnishes
• Area: above waterline, interior
• Theoretical coverage: 12-13 m²/l for 40µm DTF
• Application: brush, roll, spray gun
• Touch dry: 3 hours in temp. 20°C
• Advantages: easy application, enables quick repair

2-component topcoat high gloss paint. It protects the surface against water, maritime atmosphere, scratches and color change under the influence of UV rays. Is characte rized by high coating strength.

• Category: production, repair
• Surface: laminates, wood, steel ,aluminum
• Area: above waterline, optionaly below waterline
• Color: white, ecru, red, navy blue, blue, green, grey, black
• Theoretical coverage: 13-14 m²/l for 40µm DTF
• Application: brush, roll, spray gun
• Pot life: 3 hours
• Touch dry: 6-8 hours in temp. 20°C
• Advantages: damage resistant, permanent color, high gloss finish

2-component topcoat high gloss paint. It protects the surface against water, maritime atmosphere, scratches and color change under the influence of UV rays. Is characte rized by high coating strength.

• Category: production, repair
• Surface: laminates, wood, steel ,aluminum
• Area: above waterline, optionaly below waterline
• Color: white, ecru, red, navy blue, blue, green, grey, black
• Theoretical coverage: 13-14 m²/l for 40µm DTF
• Application: brush, roll, spray gun
• Pot life: 3 hours
• Touch dry: 6-8 hours in temp. 20°C
• Advantages: damage resistant, permanent color, high gloss finish

1-component chlorinated rubber primer, recommended as a layer increasing adhesiveness to the surface for all 1K Sea-Line paints and varnishes as a barrier surface, used directly on an old anti-fouling paint layer.

• Category: production, repair
• Surface: laminates, steel, wood, porous
• surfaces
• Area: above and below waterline
• Color: grey
• Theoretical coverage:
• 7 m²/l for 65µm DTF
• Application: brush, roll, spray gun
• Touch dry: 4hours in temp. 20°C
• Advantages: separating layer, reinforcing
• the structure of the substrate